Microstructure and mechanical properties of the Mg–Gd–Zn alloy prepared by sintering of rapidly-solidified ribbons

2022

Scientific Reports, Vol 12, Iss 1, Pp 1-12 (2022)

Abstract Mg–15Gd–1Zn (wt.%) alloy was successfully prepared via the spark plasma sintering rapid solidification ribbons process. Microstructure investigation showed that the sintered alloys consisted of fine grains, the β1 phase, and long-perioded stacking ordered phase (LPSO). The sintering temperature and time have a significant effect on the microstructural evolution. A lower sintering temperature (430 °C ) was beneficial for obtaining finer grain sizes with less than 5 μm and a higher content of β1 phase with a content of 3–15 vol.% and a size-distribution of (10–600) nm. A higher temperature for a longer sintering time, 450–470 °C and 5–10 min, helpfully promoted precipitating the abundantly lamellar LPSO phase, and its content was 2–10 vol.% for LPSO phase with the width of (10–100) nm. The mechanical properties indicated that the fine grain size and supersaturated solid solution contributed at least 50% of the yield stress, and the residual contribution was related to the β1 phase and LPSO phase strengthening, which were based on their contents and the sizes.

article

English

Nature Portfolio, 2022.

Medicine, Science