Normally, the acidic impurities in hemihydrate phosphogypsum (HPG) must be neutralized when HPG is utilized, and a little amount of calcium hydroxide (CH) is the best choice. In this paper, the effects of excessive CH (5 wt.%, 10 wt.%, 15 wt.% and 20 wt.% of HPG) for carbonation curing on the performance of hardened HPG paste were studied. According to the results of macro tests and microanalyses of XRD, TG, SEM-EDS, MIP and N2 physisorption, it could be verified that CaF2, Ca3(PO4)2 and a large amount of nanoscale CaCO3 crystals were produced as a result of neutralization and carbonation, and the compressive strength and the water resistance of carbonated HPG + CH paste were significantly improved due to the effects of nanoscale CaCO3 crystals on pore refinement and the coverage on the surfaces of gypsum crystals of the hardened paste. Therefore, this study suggests a feasible and green method for recycling HPG/PG, with the collaborative effects of neutralization, performance enhancement and reductions in CO2 emissions. [ABSTRACT FROM AUTHOR]

Copyright of Materials (1996-1944) is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)