Controlling the placement of dopants can significantly tailor graphene's properties, but this process is influenced by copper substrates during vapor deposition. Understanding the influence of interfacial atomic structures on the preference for dopant locations is crucial. In this work, we conducted a systematic first-principles study of boron- and nitrogen-doped graphene on copper {111}, considering both sublattice and superlattice configurations. Our calculations revealed that the formation energy is minimized at the top-fccb site (−0.60 eV) for boron and the hcp-fcca site (1.94 eV) for nitrogen, suggesting a possible selective distribution of dopants in both sublattice and superlattice arrangements at the graphene/copper interface. Furthermore, a lower formation energy indicates a higher release of energy during doping, resulting in a stronger interfacial binding. Since formation energy is closely associated with out-of-plane interactions, while in-plane interactions remain relatively stable, these differences offer potential avenues for modifying dopant distribution at graphene/copper interfaces. [ABSTRACT FROM AUTHOR]

Copyright of Journal of Applied Physics is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)