Surface morphology is one of the critical factors affecting the performance of electrocatalysts. Thus, with careful manipulation of the surface structures at the atomic level, the effectiveness of the catalyst can be significantly improved. Heat treatment is an effective method for inducing surface atom rearrangement, hence modifying the catalyst's characteristics. This study investigated the substrate's influence and the effect of thermal annealing on the morphology and surface reconstruction of platinum (Pt) thin-film catalysts. Our findings indicate that heat treatment in a reductive atmosphere (95% Ar + 5% H2) at 300 °C can significantly impact the degree of rearrangement of surface atoms. This process induces long-range ordering, resulting in domains with a high proportion of (111) and (100) sites without an epitaxial template. Considering that the reactivity of low-index platinum single crystals for the methanol oxidation reaction follows the following sequence Pt(111) < Pt(110) < Pt(100), increasing the proportion of (100) planes leads to a notable enhancement (up to three times) in performance, compared to untreated catalysts. Furthermore, considering the amount of precious metal consumed, a mass-specific current density obtained on annealed Pt@Ni is larger by one order of magnitude and ~2 times that obtained on Pt@Cr and Pt@GCox catalysts, respectively. Our results demonstrate that an easy-to-implement way of controlling atomic orientations improves catalyst performance. With this contribution, we propose a method for designing improved electrocatalysts, as catalytic reactions occur only at the surface. [ABSTRACT FROM AUTHOR]

Copyright of Materials (1996-1944) is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)