The pollution caused by organic dyes in water bodies has become a major environmental issue, and removing such pernicious dyes presents an immense challenge for the scientific community and governments. In this study, a sorbent based on nickel ferrite (NiFe2O4) fibers was fabricated by the solution blow spinning (SBS) method for the adsorptive removal of anionic Cong red (CR) dye. The cubic–spinel structure and the magnetic and porous nature of NiFe2O4 were confirmed by XRD, magnetometry, BET, and SEM analyses. The saturation magnetization confirmed the magnetic nature of the fibers, which favorably respond to an external magnetic field, facilitating separation from a treated solution. The sorption kinetics of CR on NiFe2O4 were best described by the pseudo-second-order model, while sorption equilibrium agreed best with the Freundlich, Langmuir, Sips, and Temkin isotherm models, suggesting a complex mechanism involving chemisorption, monolayer coverage, and heterogeneous adsorption. The NiFe2O4 fibers annealed at 500 °C showed a high CR removal efficiency of ~97% after only 30 min. The sorbent's porous structure and high specific surface area were responsible for the improved removal efficiency. Finally, the results indicated the potential of the NiFe2O4 fibers in the remediation of water contaminated with Congo red dye. [ABSTRACT FROM AUTHOR]

Copyright of Materials (1996-1944) is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)