This study presents a comprehensive assessment of the morphology and porosity of microstructured charcoal using a combination of scanning electron microscopy (SEM), computed tomography (CT), and mercury intrusion porosimetry (MIP) methods. SEM analysis revealed a parallel arrangement of tube-like structures interspersed with smaller pores, confirming the presence of fibrous formations. MIP evaluation was conducted in two research series. MIP results identified macropores as the primary contributors to mercury intrusion; however, a minor volume of mercury also intrudes to the mesopores. The total pore area was determined to range between 70.7 and 88.5 m2·g−1, with porosity values of approximately 58.0–62.4% across different experimental series. These variations highlight the heterogeneous nature of the sample. Additionally, the uniformity of the charring process during dry wood distillation was indicated by wall thickness measurements, which ranged narrowly from 5.7 to 25 µm. [ABSTRACT FROM AUTHOR]

Copyright of Materials (1996-1944) is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)