The application of hydrogen as a reducing agent in existing blast furnaces presents a promising avenue for significantly reducing emissions. The current emphasis on hydrogen reduction may necessitate a review of parameters such as the temperature, chemical composition, porosity, reduction time, and reducing agent. In this study, the impact of varying the temperature of reducing iron ore pellets in hydrogen is focused on. A mercury intrusion porosimeter is used to assess the porosity postreduction. The microstructure of the reduced pellets is analyzed with the help of scanning electron microscopy. Notably, the pore size and overall porosity are higher at higher temperatures. Using an X‐ray diffractometer, it is determined that Fe2O3 is reduced to Fe across all specified temperatures at different reduction times. The maximum degree of reduction is attained at 1000 °C while the minimum degree of reduction is attained at 700 °C. Considering these characteristics, researchers in the field can identify the optimal conditions, develop strategies, and advance technologies that contribute to the production of environmentally friendly steel. [ABSTRACT FROM AUTHOR]

Copyright of Steel Research International is the property of Wiley-Blackwell and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)