We demonstrate that single crystals of methylammonium lead bromide (MAPbBr3) could be grown directly on vertically aligned carbon nanotube (VACNT) forests. The fast-growing MAPbBr3 single crystals engulfed the protogenetic inclusions in the form of individual CNTs, thus resulting in a three-dimensionally enlarged photosensitive interface. Photodetector devices were obtained, detecting low light intensities (~20 nW) from UV range to 550 nm. Moreover, a photocurrent was recorded at zero external bias voltage which points to the plausible formation of a p-n junction resulting from interpenetration of MAPbBr3 single crystals into the VACNT forest. This reveals that vertically aligned CNTs can be used as electrodes in operationally stable perovskite-based optoelectronic devices and can serve as a versatile platform for future selective electrode development.
Comment: 16 pages, 3 figures