micro - arc oxidation, sealing treatment, electrochemical test, tensile strength, corrosion resistance, Materials of engineering and construction. Mechanics of materials, TA401-492, Technology

In order to enhance the corrosion resistance of the cast Al - Cu - Mg - Ag alloy, a micro - arc oxidation (MAO) coating was prepared on the surface of the alloy and then sealed with silicone epoxy resin. The corrosion resistance of the Al - MAO coating system before and after sealing treatment was analyzed by electrochemical test, salt spray test and full immersion test. Results showed that after the corrosion test, the cast Al - Cu - Mg - Ag alloy corroded seriously, a large number of corrosion pits appeared along the grain boundary, and the tensile strength of alloy decreased by about 60 MPa; as for the Al - MAO coating system, the corrosion medium corroded the alloy substrate through the micro pores on the surface of the coating, a large number of white spot - like corrosion products appeared on the surface, and its tensile strength decreased by about 25 MPa. The effects of sealing treatment on the Al - MAO coating were as follows: the corrosion current density reduced from 2.62×10-8A/cm2 to 5.52×10-12A/cm2; the corrosion potential positively shifted from -589 mV to -342 mV; the low - frequency impedance increased from～105 Ω·cm2 to ～109 Ω·cm2; after the salt spray test and the full immersion test, no corrosion occurred; and the tensile strength basically remained the same. After the sealing treatment, the surface defects of the MAO coating were sealed, and a dense ceramic - organic composite coating formed on the alloy surface, which greatly reduced the corrosion rate and significantly improved the corrosion resistance of the alloy system.