Ti/steel bonding, Interlayer, Interfacial strength, Intermetallic compounds (IMCs), Hot-compression bonding(HCB), Mining engineering. Metallurgy, TN1-997

In this study, the TA3/L907A titanium-steel clad plates with or without interlayers were fabricated via HCB and the interfacial microstructure, and shear strength were investigated in detail. A reaction layer mixed by Fe–Ti interphases and TiC formed at the TA3/L907A interface and the formation of brittle intermetallic compounds (IMCs) severely deteriorated the interfacial properties, which resulted in a low shear strength of 192 MPa. To improve the shear strength, Ni foil, Nb foil, and Nb + Ni foils were respectively added as interlayer between TA3 and L907A. With interlayers, no visible Fe–Ti–C IMCs were detected at the interface, which suggests that interlayers effectively prohibited the inter-diffusion of these elements. Although Ni or Nb interlayer respectively elevated the interfacial shear strength to 333 MPa and 359 MPa, weak-bonded features such as lamellar Ni–Ti interphases and Fe2Nb IMC still existed, making cracks tend to initiate at these regions. Further adding Nb + Ni double interlayers achieved the highest shear strength of 422 MPa. The enhancement in property can be attributed to solid solution regions at both Ti/Nb and Ni/Steel interfaces without IMC or void, and the discontinuous distributed olive-like δ-Ni3Nb precipitation at the Nb/Ni interface.