In order to prepare diamond composites with excellent mechanical properties under non-extreme conditions, in this study, a diamond–ceramic composite was successfully prepared via reactive spark plasma sintering using a diamond–Ti–Si powder mixture as the raw material. The microstructures and mechanical properties of the diamond–ceramic composite sintered at different temperatures were studied. When the sintering temperature was 1500 °C, the diamond–ceramic composite exhibited a volume density of 3.65 g/cm3, whereas the bending strength and fracture toughness were high at 366 MPa and 6.17 MPa·m1/2, respectively. In addition, variable-temperature sintering activated the chemical reaction at a higher temperature, whereas lowering the temperature prevented excessive graphitisation, which is conducive to optimising the microstructure and mechanical properties of the composite.