coal fly ash, lithium, ion sieve, adsorption, Technology, Engineering (General). Civil engineering (General), TA1-2040, Biology (General), QH301-705.5, Physics, QC1-999, Chemistry, QD1-999

The present study focuses on the synthesis of a manganese dioxide lithium ion sieve and its application for the extraction of lithium from coal fly ash. The preparation and adsorption experiments of the manganese dioxide lithium ion sieve were carried out using the orthogonal method, while the HCl elution experiment was carried out using the single factor method. The results showed that the optimum preparation conditions under which the average lithium adsorption efficiency reached 99.98% were a 10:1 mass ratio of manganese dioxide to lithium hydroxide, calcination at 800 °C for 60 min, 1.5 mol/L HCl, soaking for 24 h and stirring for 18 h. Additionally, the optimum adsorption efficiency was observed with an adsorption time of 30 min, KOH pH of 8 and KOH scrubbing time of 10 min, resulting in 100% lithium adsorption efficiency. The optimum elution conditions for lithium were determined to be an HCl concentration of 0.01 mol/L and an elution time of 40 min, giving 100% lithium elution efficiency.